Gorgan University Of Agricultural Sciences and Natural Resources Journal of Wood and Forest Science and Technology 2322-2077 19 2 2012 12 08 Thermal dependence of thermal conductivity of particleboard containing Ag and Cu nanoclouids Thermal dependence of thermal conductivity of particleboard containing Ag and Cu nanoclouids 131 142 961 FA Journal Article 2012 12 08 The purpose of this study was to investigate the effect of silver and copper nanoclouids on the thermal conductivity of particleboard. For this purpose, nanoclouids with concentration of 4000 (ppm) in four levels of 0, 5, 10 and 15% were applied to the particleboards with the consumed resin, then thermal conductivity of the boards were measured at four temperature profiles (45, 50, 55 and 60 °C). The results showed that with increasing nanoclouids content, the thermal conductivity increased, and the samples containing silver nanoclouids indicate higher thermal conductivity than the samples containing copper nanoclouids at the same conditions. With increasing temperature, thermal conductivity of the boards increased. The increased of thermal conductivity of compact wooden plates was as a positive factor in production process in terms of cost reducing and increase efficiency of the products. The purpose of this study was to investigate the effect of silver and copper nanoclouids on the thermal conductivity of particleboard. For this purpose, nanoclouids with concentration of 4000 (ppm) in four levels of 0, 5, 10 and 15% were applied to the particleboards with the consumed resin, then thermal conductivity of the boards were measured at four temperature profiles (45, 50, 55 and 60 °C). The results showed that with increasing nanoclouids content, the thermal conductivity increased, and the samples containing silver nanoclouids indicate higher thermal conductivity than the samples containing copper nanoclouids at the same conditions. With increasing temperature, thermal conductivity of the boards increased. The increased of thermal conductivity of compact wooden plates was as a positive factor in production process in terms of cost reducing and increase efficiency of the products. https://jwfst.gau.ac.ir/article_961_047cc4d8be033ace9240a04d5b3e7ae1.pdf